title = "Thermooxidative aging studies on silicone rubber and lifetime prediction",
abstract = "Silicone rubber have been aged in air while under 25\% compression at temperature up to 250°C. These studies examined the compression set of silicone rubber at accelerated (elevated) temperatures and were then used to make predictions about compression set at room temperature. The data obtained could be amenable to time-temperature superposition and Arrhenius treatment. The results suggest the presence of two degradation processes with activation energies of 71.6 kJ mol-1 (for temperatures above 165 °C) and 26.08 kJ mol-1 (for temperatures below 165 °C). Based on the extrapolation of the non-Arrhenius behavior, it was estimated that significant compression set loss would occur after around 67 years at 25 °C.",
keywords = "Activation energy, Aging, Compression set, Lifetime prediction, Non-Arrhenius, Silicone rubber",
author = "Wang, \{You Shan\} and Jiang, \{Sha Sha\} and Liu, \{Yu Peng\}",
year = "2013",
doi = "10.4028/www.scientific.net/AMR.777.11",
language = "英语",
isbn = "9783037857946",
series = "Advanced Materials Research",
pages = "11--14",
booktitle = "Environmental Biotechnology and Materials Engineering 2013",
note = "2013 International Conference on Environmental Biotechnology and Materials Engineering, EBME 2013 ; Conference date: 23-08-2013 Through 25-08-2013",
}