title = "The residual tensile properties after impact of CFRP with different porosities",
abstract = "The effects of voids on the residual tensile strength after impact of CFRP laminates were discussed in this paper. Impact tests on the CFRP laminates with two porosity levels were conducted at five impact energy levels of 3J, 6J, 9J, 12J and 15J at the room temperature. The tensile strength and the tensile modulus of non-impacted specimens decreased 0.67\% and 0.086\% with the porosity increasing from 0.33\% to 0.71\%. Compared to non-impact specimens, the residual tensile strength after impact (TAI) and tensile modulus after impact significantly decrease with increasing impact energy. The void contents had the negative effects on the residual tensile strength after impact and tensile modulus after impact of the specimens at the same impact energy.",
keywords = "Carbon fiber, Impact, Laminates, Porosity, Tensile strength",
author = "Aying Zhang and Dongxing Zhang",
year = "2013",
doi = "10.4028/www.scientific.net/AMR.634-638.2085",
language = "英语",
isbn = "9783037855898",
series = "Advanced Materials Research",
number = "1",
pages = "2085--2088",
booktitle = "Advances in Chemical, Material and Metallurgical Engineering",
edition = "1",
note = "2012 2nd International Conference on Chemical, Material and Metallurgical Engineering, ICCMME 2012 ; Conference date: 15-12-2012 Through 16-12-2012",
}