title = "The residual bending properties after impact of CFRP laminates with voids",
abstract = "The effects of voids on the residual bending strength after impact of CFRP laminates were discussed in this paper. Impact tests on the CFRP laminates with two porosity levels were conducted at five impact energy levels of 3J, 6J, 9J, 12J and 15J at the room temperature. The bending strength and the bending modulus of non-impacted specimens decreased 0.67\% and 0.086\% with the porosity increasing from 0.33\% to 0.71\%. Compared to non-impact specimens, the residual bending strength after impact (BAI) and bending modulus after impact significantly decrease with increasing impact energy. The void contents had the negative effects on the BAI after impact of the specimens at the same impact energy, while no obvious effects of void contents on the bending modulus are observed.",
keywords = "Bending strength, Carbon fiber, Impact, Laminates, Porosity",
author = "Aying Zhang and Dongxing Zhang",
year = "2013",
doi = "10.4028/www.scientific.net/AMR.634-638.2081",
language = "英语",
isbn = "9783037855898",
series = "Advanced Materials Research",
number = "1",
pages = "2081--2084",
booktitle = "Advances in Chemical, Material and Metallurgical Engineering",
edition = "1",
note = "2012 2nd International Conference on Chemical, Material and Metallurgical Engineering, ICCMME 2012 ; Conference date: 15-12-2012 Through 16-12-2012",
}