The dislocation sub-structure evolution during hot compressive deformation of Ti-6Al-2Zr-1Mo-1V alloy at 800 °c

Hot compressive behaviors of Ti-6Al-2Zr-1Mo-1V alloy at 800 °C, as well as the evolution of microstructure during deformation process, were investigated. The experimental results show that flow stress increases to a peak stress followed by a decease with increasing strain, and finally forms a stable stage. Dislocations are generated at the interface of α/β phase, and the phase interface and dislocation loops play an important role in impeding the movement of dislocation. As strain increasing, micro-deformation bands with high-density dislocation are formed, and dynamic recrystallizaton occurs finally. XRD Fourier analysis reveals that dislocation density increases followed by a decrease during compressive deformation, and falls into the range from 10¹⁰ to 10¹¹ cm^-2.