Study on synthesis of poly(N-vinyl carbazole) with azo chromophore side groups

Wen Long Zhang; Hong Zhao; Xuan Wang; Yu Ping Wen; Yong Ping Bai

Study on synthesis of poly(N-vinyl carbazole) with azo chromophore side groups

Wen Long Zhang^*
, Hong Zhao
, Xuan Wang
, Yu Ping Wen
, Yong Ping Bai

^*Corresponding author for this work

School of Chemistry and Chemical Engineering

Harbin University

Research output: Contribution to journal › Article › peer-review

Abstract

The synthesis of Poly(N-vinyl carbazole) with azo chromophore side groups was studied. Poly(N-vinyl carbazole) was modified to prepare azo-PVK by post-azo-coupling reaction with diazo salt as raw material using phase-transfer catalysts. The molar mass proportion of PVK and diazo salt is 1:4. Diazo salt was divided into several parts and added into solution in batches at room temperature to react for 96 hours. It was confirmed that diazo groups had been grafted to PVK by analyzing IR and UV-vis data.

Original language	English
Pages (from-to)	657-660
Number of pages	4
Journal	Cailiao Kexue yu Gongyi/Material Science and Technology
Volume	14
Issue number	6
State	Published - Dec 2006

Keywords

Chromophore group
Diazo salt
Poly(N-vinyl carbazole)

Cite this

@article{447a67f940e2455f8e9667803df6c5c6,

title = "Study on synthesis of poly(N-vinyl carbazole) with azo chromophore side groups",

abstract = "The synthesis of Poly(N-vinyl carbazole) with azo chromophore side groups was studied. Poly(N-vinyl carbazole) was modified to prepare azo-PVK by post-azo-coupling reaction with diazo salt as raw material using phase-transfer catalysts. The molar mass proportion of PVK and diazo salt is 1:4. Diazo salt was divided into several parts and added into solution in batches at room temperature to react for 96 hours. It was confirmed that diazo groups had been grafted to PVK by analyzing IR and UV-vis data.",

keywords = "Chromophore group, Diazo salt, Poly(N-vinyl carbazole)",

author = "Zhang, \{Wen Long\} and Hong Zhao and Xuan Wang and Wen, \{Yu Ping\} and Bai, \{Yong Ping\}",

year = "2006",

month = dec,

language = "英语",

volume = "14",

pages = "657--660",

journal = "Cailiao Kexue yu Gongyi/Material Science and Technology",

issn = "1005-0299",

publisher = "Harbin Institute of Technology",

number = "6",

}

TY - JOUR

T1 - Study on synthesis of poly(N-vinyl carbazole) with azo chromophore side groups

AU - Zhang, Wen Long

AU - Zhao, Hong

AU - Wang, Xuan

AU - Wen, Yu Ping

AU - Bai, Yong Ping

PY - 2006/12

Y1 - 2006/12

N2 - The synthesis of Poly(N-vinyl carbazole) with azo chromophore side groups was studied. Poly(N-vinyl carbazole) was modified to prepare azo-PVK by post-azo-coupling reaction with diazo salt as raw material using phase-transfer catalysts. The molar mass proportion of PVK and diazo salt is 1:4. Diazo salt was divided into several parts and added into solution in batches at room temperature to react for 96 hours. It was confirmed that diazo groups had been grafted to PVK by analyzing IR and UV-vis data.

AB - The synthesis of Poly(N-vinyl carbazole) with azo chromophore side groups was studied. Poly(N-vinyl carbazole) was modified to prepare azo-PVK by post-azo-coupling reaction with diazo salt as raw material using phase-transfer catalysts. The molar mass proportion of PVK and diazo salt is 1:4. Diazo salt was divided into several parts and added into solution in batches at room temperature to react for 96 hours. It was confirmed that diazo groups had been grafted to PVK by analyzing IR and UV-vis data.

KW - Chromophore group

KW - Diazo salt

KW - Poly(N-vinyl carbazole)

UR - https://www.scopus.com/pages/publications/33846827198

M3 - 文章

AN - SCOPUS:33846827198

SN - 1005-0299

VL - 14

SP - 657

EP - 660

JO - Cailiao Kexue yu Gongyi/Material Science and Technology

JF - Cailiao Kexue yu Gongyi/Material Science and Technology

IS - 6

ER -

Study on synthesis of poly(N-vinyl carbazole) with azo chromophore side groups

Abstract

Keywords

Other files and links

Fingerprint

Cite this