Abstract
The nano and micro WC-17Co coatings were fabricated on the 0Cr13Ni5Mo stainless steel by supersonic plasma spraying. Their porosity, adhesive strength, hardness and wear resistance of both coatings were compared. The results indicate that the porosity (0.56%) and adhesive strength (over 69.2 MPa) of the nano-coating are higher than those of the micro-coating. The hardness of the nano-coating and the micro-coating are 3.9 and 3.8 times more than that of matrix, respectively. The hardness of both coatings gradually increases from top to bottom. The wear mechanisms of matrix are adhesive wear, abrasive wear and delamination, while the coatings only suffers adhesive wear. The lower porosity, higher hardness and stronger compressive resistance of the nano-coating result in its excellent wear resistance.
| Original language | English |
|---|---|
| Pages (from-to) | 807-811 |
| Number of pages | 5 |
| Journal | Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering |
| Volume | 46 |
| Issue number | 3 |
| State | Published - 1 Mar 2017 |
Keywords
- Nano-coating
- Supersonic plasma spraying
- WC-17Co
- Wear
Fingerprint
Dive into the research topics of 'Properties of Supersonic Plasma Sprayed WC-17Co Nano-coating'. Together they form a unique fingerprint.Cite this
- APA
- Author
- BIBTEX
- Harvard
- Standard
- RIS
- Vancouver