Microstructure and mechanical properties of tantalum carbide ceramics: Effects of Si₃N₄ as sintering aid

Stoichiometric Tantalum carbide (TaC) ceramics were prepared by reaction spark plasma sintering using 0.333–2.50 mol% Si₃N₄ as sintering aid. Effects of the Si₃N₄ addition on densification, microstructure and mechanical properties of the TaC ceramics were investigated. Si₃N₄ reacted with TaC and tantalum oxides such as Ta₂O₅ to form a small concentration of tantalum silicides, SiC and SiO₂, with significant decrease in oxygen content in the consolidated TaC ceramics. Dense TaC ceramics having relative densities >97% could be obtained at 0.667% Si₃N₄ addition and above. Average grain size in the consolidated TaC ceramics decreased from 11 µm at 0.333 mol% Si₃N₄ to 4 µm at 2.50 mol% Si₃N₄ addition. The Young's modulus, Vickers hardness and flexural strength at room temperature of the TaC ceramic with 2.50 mol% Si₃N₄ addition was 508 GPa, 15.5 GPa and 605 MPa, respectively. A slight decrease in bending strength was observed at 1200 °C due to oxidation of the samples.