Microstructure and mechanical properties of SiC Whisker reinforced ZrO₂–Y₂O₃ composites

The mechanical properties of 20 vol.-%SiC whisker reinforced ZrO₂−V₂O₃ composites containing 2 and 6 mol.-% Y₂O₃ were measured at room temperature and the fracture surface was examined. The results indicate that the mechanical behaviour of the composites is strongly influenced by the Y₂O₃ content. The magnitude of the enhancement of the toughness in composites containing 2 mol.-% Y₂O₃ compared with unreinforced ZrO₂−Y₂O₃ matrix is larger than that for the composites containing 6 mol.-% Y₂O₃. Crack propagation modes were characterised by crack deflection, whisker bridging, and whisker pullout. High resolution electron microscopic observations show that in composites containing 2 mol.-% Y₂O₃ the whiskers are directly bonded to the matrix. However, in composites containing 6 mol.-% Y₂O₃ there is always a thick amorphous layer at the interface, indicating that the high Y₂O₃ content has promoted the formation of interfacial amorphous layers. These interfacial amorphous layers strengthen the interfacial bonding, resulting in a composite with a low fracture toughness.