Microstructure and mechanical properties of ceramics obtained from chemically co-precipitated Al₂O₃-GdAlO₃ nano-powders with eutectic composition

An efficient and flexible chemical co-precipitation method has been used to synthesize nanoscale Al₂O₃-GdAlO₃ powders with eutectic composition. The as-synthesized powders exhibit a highly dispersive and homogeneous distribution with an average particle size of 50 nm. The phase transition in the resulting powders strongly depends upon the calcination temperature. GdAlO₃ undergoes complete crystallization after calcination at 1050 °C, however, the diffraction peaks of α-Al₂O₃ are found at a relatively high calcination temperature of at least 1300 °C. The fully-densified Al₂O₃-GdAlO₃ ceramic with eutectic composition obtained by hot pressing the nanoscale powders at 1500 °C exhibits a room temperature flexural strength of 556 MPa, a Vickers hardness of 17.3 GPa and a fracture toughness of 7.5 MPa m^1/2. The high temperature flexural strength of the as-sintered Al₂O₃-GdAlO₃ ceramic is measured to be 515 MPa after bending tests at 1000 °C.