Microstructural evolution, mechanical and thermal properties of LaB₆ embedded in Si-B-C-N prepared by spark plasma sintering

Si-B-C-N monoliths with 5 wt% LaB₆ additives were prepared by spark plasma sintering at 1250–2000 °C and 50 MPa using a mechanically alloyed mixture of graphite, c-Si, h-BN and LaB₆ powders as the starting materials. Microstructural evolution, mechanical and thermal properties of the as-prepared La/Si-B-C-N monoliths were investigated. The densification of the ceramics starts at 1160° and ends at 1800 °C with the formation of La-containing compounds coupled with SiC and BN(C) phases. La-containing BN(C) grains develop into a lamellar structure at 1900 °C offering improved fracture toughness and decreased Vickers hardness, flexural strength and elastic modulus. The formation of lamellar BN(C) is also responsible for a high thermal expansion coefficient of 4.2×10⁻⁶ /°C.