Investigation of the microwave dielectric properties of the Li_4x/3Zn_2−2xTi_1+2x/3O₄ system by P–V–L theory and vibration spectroscopy

Li_4x/3Zn_2–2xTi_1+2x/3O₄ microwave dielectric ceramics with a spinel phase were prepared via a high-temperature solid-phase method. P–V–L theory, vibration spectra, and XPS were utilized to establish the links between the intrinsic and extrinsic factors and the microwave dielectric properties. According to the characterization, the change in permittivity (ε_r) was ascribed to the increase in the average bond ionicity of Ti–O(Af_iTi-O) and the polar mode of the lattice vibration; the change in quality factor(Q × f) resulted from the change in the Ti–O lattice energy (AU_Ti-O) and existence of oxygen vacancy; the increase in temperature coefficient of the resonance frequency (τ_f) was triggered by the increase in the Ti–O bond energy. The Li_0.6Zn_1.1Ti_1.3O₄ ceramics (x = 0.45) sintered at 1125 °C finally obtained optimal microwave dielectric constants of ε_r = 17.3, Q × f = 76,318 GHz and τ_f = -58 ppm/°C.