title = "Interfacial microstructure and phase constitution of the Cu/Al dissimilar metals joint made by contact reactive brazing",
abstract = "Joining Cu to Al has been carried out by vacuum contact reactive brazing without filler metal. Experimental results obtained showed that the eutectic structure and some Cu-Al intermetallic compounds were the main phases of the braze seam. The fracture surface of the joint presented typical brittle fracture for the existence of intermetallic compounds at the interface and the shear strength could reach 65MPa.",
keywords = "Contact reactive brazing, Interface, Microstructure, Shear strength",
author = "Hongtao Zhang and Jian Cao and Hao Lu",
year = "2010",
doi = "10.4028/www.scientific.net/AMR.97-101.3891",
language = "英语",
isbn = "0878492801",
series = "Advanced Materials Research",
pages = "3891--3894",
booktitle = "Manufacturing Science and Engineering I",
note = "2009 International Conference on Manufacturing Science and Engineering, ICMSE 2009 ; Conference date: 26-12-2009 Through 28-12-2009",
}