High- and Low-Temperature Deformation Behavior of Different Orientation Hot-Rolled Annealed Zircaloy-4

In this paper, the hot-rolled annealed Zircaloy-4 samples with different orientation were subjected to uniaxial compression with a strain rate of 0.001 s⁻¹ to obtain the stress-strain curves of different initial orientation samples at different temperatures. Electron backscatter diffraction (EBSD) technique and transmission electron microscope (TEM) technique were used to analyze the microstructures and textures of compressed samples. The mechanical properties and microstructural evolution of rolling directions (RD), transverse directions (TD) and normal directions (ND) were investigated under the conditions of – 150 °C low temperature, room temperature and 200 °C high temperature (simulated lunar temperature environment). The results show that the strength of Zircaloy-4 decreases with the increase in deformation temperature, and the strength in three orientations is ND CloseSPigtSPi TD CloseSPigtSPi RD. The deformation mechanism of hot-rolled annealed Zircaloy-4 with different orientation is different. In RD, {10 1 ¯ 0} 〈 a 〉 prismatic slip has the highest Schmid factor (SF), so it is most easy to activate the slip, followed by TD orientation, and ND orientation is the most difficult to activate. The deformed grains abide slip→twinning→slip rule, and the different orientation Zircaloy-4 deformation mechanisms mainly are the twinning coordinated with the slip.