Fabrication of hybrid CoMoO₄–NiMoO₄ nanosheets by chitosan hydrogel assisted calcinations method with high electrochemical performance

Herein, hybrid CoMoO₄–NiMoO₄ nanosheets (NSs) with mesoporous morphology were assembled using a chitosan hydrogel assisted calcination method. This unique architecture provides numerous channels for rapid diffusion of electrolyte ions, fast electron transfer and high electrochemical activity due to the synergistic effect between the CoMoO₄ and NiMoO₄. The assembled CoMoO₄–NiMoO₄ hybrid material can be a very good supercapacitor electrode, due to its high specific capacitance of 1940 F g⁻¹ at the current density of 1 A g⁻¹. Even at a current density as high as 20 A g⁻¹, the CoMoO₄–NiMoO₄ electrode still delivers a high specific capacitance of 1280 F g⁻¹, indicating its superior rate of specific capacitance 65.98% and excellent cycling stability with capacitance retention 99% after 5000 cycles. Furthermore, the as-prepared CoMoO₄–NiMoO₄ was employed as anode and activated carbon was used as cathode for solid-state asymmetric supercapacitor. Asymmetric supercapacitors with high power density and energy density (53.33 W h kg⁻¹ at a power density of 800 W kg⁻¹) were realized by improving the potential window with the voltage range from 0 to 1.6 V. These results indicate that the CoMoO₄–NiMoO₄ electrode shows potential application for high performance, environmentally friendly, and low-cost energy storage device. [Figure not available: see fulltext.]