Evaluation of the properties of Si3N4/Si3N4 joint brazed using a filler alloy containing Pd

M. Naka; Jie Zhang; Yu Zhou

Evaluation of the properties of Si₃N₄/Si₃N₄ joint brazed using a filler alloy containing Pd

M. Naka
, Jie Zhang^*
, Yu Zhou

^*Corresponding author for this work

The University of Osaka
Harbin Institute of Technology

Research output: Contribution to journal › Article › peer-review

Abstract

Si₃N₄ ceramic was jointed to itself using a filler alloy of Cu76.5Pd8.5Ti15, and the mechanical properties of the joint were measured and analyzed. By using a filler alloy of Cu76.5Pd8.5Ti15, the Si₃N₄/Si₃N₄ joints were obtained by brazing at 1373-1473 K for 0.9-5.4 ks under a pressure of 2×10^-3 MPa. The effect of brazing parameters on the shear strength of the joint was investigated. When the brazing temperature and the holding time is 1423 K and 5.4 ks respectively, the 198 MPa maximum shear strength of the Si₃N₄/Si₃N₄ joint is obtained.

Original language	English
Pages (from-to)	187-188
Number of pages	2
Journal	Journal of Materials Science and Technology
Volume	19
Issue number	SUPPL.
State	Published - Dec 2003
Externally published	Yes

Keywords

Active brazing
Ci-Pd-Ti filler alloy
Shear strength
SiN ceramic

Cite this

@article{6a8f8d49fbae47e9a804dbdcbe400725,

title = "Evaluation of the properties of Si3N4/Si3N4 joint brazed using a filler alloy containing Pd",

abstract = "Si3N4 ceramic was jointed to itself using a filler alloy of Cu76.5Pd8.5Ti15, and the mechanical properties of the joint were measured and analyzed. By using a filler alloy of Cu76.5Pd8.5Ti15, the Si3N4/Si3N4 joints were obtained by brazing at 1373-1473 K for 0.9-5.4 ks under a pressure of 2×10-3 MPa. The effect of brazing parameters on the shear strength of the joint was investigated. When the brazing temperature and the holding time is 1423 K and 5.4 ks respectively, the 198 MPa maximum shear strength of the Si3N4/Si3N4 joint is obtained.",

keywords = "Active brazing, Ci-Pd-Ti filler alloy, Shear strength, SiN ceramic",

author = "M. Naka and Jie Zhang and Yu Zhou",

year = "2003",

month = dec,

language = "英语",

volume = "19",

pages = "187--188",

journal = "Journal of Materials Science and Technology",

issn = "1005-0302",

publisher = "Chinese Society of Metals",

number = "SUPPL.",

}

TY - JOUR

T1 - Evaluation of the properties of Si3N4/Si3N4 joint brazed using a filler alloy containing Pd

AU - Naka, M.

AU - Zhang, Jie

AU - Zhou, Yu

PY - 2003/12

Y1 - 2003/12

N2 - Si3N4 ceramic was jointed to itself using a filler alloy of Cu76.5Pd8.5Ti15, and the mechanical properties of the joint were measured and analyzed. By using a filler alloy of Cu76.5Pd8.5Ti15, the Si3N4/Si3N4 joints were obtained by brazing at 1373-1473 K for 0.9-5.4 ks under a pressure of 2×10-3 MPa. The effect of brazing parameters on the shear strength of the joint was investigated. When the brazing temperature and the holding time is 1423 K and 5.4 ks respectively, the 198 MPa maximum shear strength of the Si3N4/Si3N4 joint is obtained.

AB - Si3N4 ceramic was jointed to itself using a filler alloy of Cu76.5Pd8.5Ti15, and the mechanical properties of the joint were measured and analyzed. By using a filler alloy of Cu76.5Pd8.5Ti15, the Si3N4/Si3N4 joints were obtained by brazing at 1373-1473 K for 0.9-5.4 ks under a pressure of 2×10-3 MPa. The effect of brazing parameters on the shear strength of the joint was investigated. When the brazing temperature and the holding time is 1423 K and 5.4 ks respectively, the 198 MPa maximum shear strength of the Si3N4/Si3N4 joint is obtained.

KW - Active brazing

KW - Ci-Pd-Ti filler alloy

KW - Shear strength

KW - SiN ceramic

UR - https://www.scopus.com/pages/publications/3242746003

M3 - 文章

AN - SCOPUS:3242746003

SN - 1005-0302

VL - 19

SP - 187

EP - 188

JO - Journal of Materials Science and Technology

JF - Journal of Materials Science and Technology

IS - SUPPL.

ER -

Evaluation of the properties of Si₃N₄/Si₃N₄ joint brazed using a filler alloy containing Pd

Abstract

Keywords

Other files and links

Fingerprint

Cite this