Enhanced Thermal Decomposition Properties and Catalytic Mechanism of Ammonium Perchlorate over CuO/MoS₂ Composite

In this report, CuO/MoS₂ composites were successfully prepared by the hydrothermal method where nano-sized CuO was uniformly distributed on the surface of hierarchical MoS₂ substrates (CuO/MoS₂ composites). Their physicochemical properties and catalytic performance in ammonium perchlorate (AP) decomposition were investigated and characterized by XRD, SEM, TEM, BET, XPS, TG/DSC and combustion measurement. The results showed that it could decrease AP decomposition temperature at high decomposition stage from 416.5 °C to 323.5 °C and increase the heat release from 378 J/g (pure AP) to 1340 J/g (AP with catalysts), which was better than pure CuO nanoparticles (345.5 °C and 1046 J/g). Meanwhile, it showed excellent performance in combustion reaction either in N₂ or air atmosphere. The results obtained by photocurrent spectra, photoluminescence spectra and time-resolved fluorescence emission spectra indicated that loading CuO mediated the generation rate and combination rate of electrons and holes, thus tuning the catalytic performance on AP decomposition. This study proved that employing the supports that can synergistically interact with CuO is an efficient strategy to enhance the catalytic performance of CuO.