Effects of the prefabricated Cu-Ti Film on the microstructure and mechanical properties of the multiphase coating by thermo plasma nitriding on C17200 Cu alloy

To improve the surface wear resistance, plasma nitriding of the prefabricated Cu-Ti films on the C17200 Cu alloy is performed to investigate the effects of the composition of the Cu-Ti films on the microstructure and the mechanical properties of the modified surface. The results firstly showed that obvious microstructure evolution appeared during the thermo-plasma nitriding process, where both the surface morphology of the composed phases and the cross-sectional profiles of the multiphase coatings varied for the three types of films. Small amounts of Ti-N compounds, Be₃Ti₂Cu, and different types of Cu-Ti intermetallics formed in the multiphase coating after plasma nitriding, which is dependent on the composition of the prefabricated Cu-Ti film. Correspondingly, the surface hardness and the wear resistance of the C17200 Cu substrates were obviously improved, with the obtained adhesive strength of the substrate reaching a satisfactory range.