title = "Effects of heat treatment and sintering temperature on the microstructure of TiBw/Ti60 composites with a novel network microstructure",
abstract = "In order to improve the high temperature mechanical properties of titanium matrix composites (TMCs), in situ TiB whiskers reinforced Ti60 (TiBw/Ti60) composites with a novel network microstructure were fabricated. Coarse and anisotropic TiB whiskers were observed at high sintering temperature of 1300 oC, while many unreacted TiB2 particles were still detected at the sintering temperature of 1200 oC. The strength of the composites sintered at the temperature of 1300 oC increased from 1030MPa to 1093MPa, and the tensile fracture elongation increased from 1.6\% to 2.5\% compared with those fabricated at 1200 oC. The solution treatment (1100 oC/4hrs/WQ) could effectively reduce the element segregation formed in the sintering process. After solution treatment, both the strength and elongation of the composites remarkably increased from 1093MPa to 1190MPa and 2.5\% to 4\%, respectively.",
keywords = "Heat treatment, Precipitation, Sintering temperature, Titanium matrix composites",
author = "B. Wang and Huang, \{L. J.\} and Liu, \{B. X.\} and L. Geng",
year = "2014",
language = "英语",
series = "16th European Conference on Composite Materials, ECCM 2014",
publisher = "European Conference on Composite Materials, ECCM",
booktitle = "16th European Conference on Composite Materials, ECCM 2014",
note = "16th European Conference on Composite Materials, ECCM 2014 ; Conference date: 22-06-2014 Through 26-06-2014",
}