Effect of water-oil ratio on the photocatalytic performance of visible light-active BiVO₄ nanoparticles prepared by inverse microemulsion-calcination method

Nowadays, nano-photocatalysts (NPs) have become the research focus in the field of photocatalysis due to their excellent photocatalytic activity, and microemulsion is an effective method to prepare high-efficiency nano-photocatalysts. Here, BiVO₄ NPs with high efficiency under visible light were prepared by a combination of reverse microemulsion method and calcination method. XRD, SEM, TEM, XPS, DRS, PL, BET and other characterization tests were used to comprehensively explore the influence of water-oil ratio on the physicochemical properties of the catalysts. The results show that BiVO₄ NPs of monoclinic scheelite with high crystallization degree can be obtained by this method. The microscopic morphology, specific surface area and total pore volume of BiVO₄ NPs are significantly affected by the water-oil ratio. It is difficult to obtain BiVO₄ NPs with small particle size and uniform dispersion under the condition of too low or too high water-oil ratio. Meanwhile, the photogenerated carrier recombination efficiency of the catalyst is significantly improved, thus reducing the photocatalytic activity of the catalyst. Strikingly, the BiVO₄ NPs obtained under the condition of water-oil ratio is 20 exhibited well-dispersed nanospheres with diameters ranging from 80 to 100 nm. It has the highest photocatalytic activity due to its high crystallinity, large specific surface area and total pore volume and relatively low photogenerated carrier recombination efficiency. Under visible light irradiation, the degradation efficiency of RhB can reach 97.69% in 100 min, and the rate constant is 0.03253 min⁻¹.