Effect of porosity on hydrogenation kinetics of Mg-3Ni-2MnO₂ nanocomposite powder reaction bed

Hydrided Mg-3Ni-2MnO₂ composite powders were fabricated by reactive ball milling with hydrogen, and accumulative hydrogenation kinetics and temperature field of reaction bed with various porosities (0.37, 0.53 and 0.63) were measured. The results show that the accumulative hydrogenation kinetics of Mg-3Ni-2MnO₂ powder reaction bed depends strongly on the effect of heat transfer, mass transfer and intrinsic reaction together. The reaction bed with the porosity of 0.53 exhibits the largest hydrogenation rate. During the hydrogenation process, the temperature of reaction bed rises quickly due to the fast release of heat, and the temperature difference between center and wall with 0.53 porosity can keep high even for a long time, which promotes fast heat transfer. The further analysis indicates that more emphases should be put on heat transfer rate rather than the only improvement of the effective thermal conductivity.