title = "Effect of MgO coating on whisker preform strength of aluminum matrix composite fabricated by squeeze casting",
abstract = "In this paper, MgO with different contents was coated on the surface of magnesium borate whisker using chemical precipitation method. The resistance to compression of whisker perform was measured, and the effect of MgO coating on the deformation resistance of magnesium borate whisker perform was studied. The result shows that the compression strength of whisker perform sintered at 900 °C was enhanced with increasing MgO coating ratio to magnesium borate whisker. The compression strength was increased from 0.80MPa for coating ratio of 0 to 1.34Mpa for coating ratio of 1:10. Then magnesium borate whisker-reinforced pure aluminum (MBOw/Al) composite without apparent microscopic defects was fabricated using modified whisker perform. The tensile strength and elastic modulus at room temperature attain 240MPa and 130GPa, respectively.",
keywords = "Metal matrix composites, MgO coating, Perform, Squeeze casting",
author = "Lei Zhang and Zhang, \{Rui Wu\} and Wang, \{Li Dong\} and Qiao, \{Ying Jie\} and Xu, \{Shi Chong\} and Fei, \{Wei Dong\}",
year = "2013",
doi = "10.4028/www.scientific.net/AMR.750-752.2126",
language = "英语",
isbn = "9783037857632",
series = "Advanced Materials Research",
pages = "2126--2130",
booktitle = "Advanced Engineering Materials III",
note = "3rd International Conference on Advanced Engineering Materials and Technology, AEMT 2013 ; Conference date: 11-05-2013 Through 12-05-2013",
}