Effect of lanthanum ions on magnetic properties of Y₃Fe ₅O₁₂ nanoparticles

Lanthanum ion (La³⁺)-substituted garnet nanoparticles Y _3-x La _x Fe₅O₁₂ (x = 0.0, 0.2, 0.4, 0.6, 0.8, and 1.0) were fabricated by a sol-gel method. Their crystalline structures and magnetic properties were investigated by using X-ray diffraction (XRD), vibrating sample magnetometer (VSM), and Mössbauer spectrum. The XRD results show that samples of Y_3-x La _x Fe ₅O₁₂ (0.0 ≤ x ≤ 0.8) are all single phase and the sizes of particles range from 32 to 65 nm. Those of Y₂LaFe ₅O₁₂ consisted of peaks from garnet and LaFeO₃ structures. Compared to pure YIG, the saturation magnetization is larger when the La concentration x = 0.2. However, with increasing La concentration (x), it decreases obviously. Meanwhile, may be due to the enhancement of the surface spin effects, the saturation magnetization rises as the particle size is increased. Different from the pure YIG, the Mössbauer spectra of Y _2.8La_0.2Fe₅O₁₂ and Y _2.2La_0.8Fe₅O₁₂ are composed of four sets of six-line hyperfine patterns. The results tell us that the substitution of La³⁺ ions with large ionic radius (1.061 Å) will give rise to a microscopic structure distortion of the a- and d-sites to different degrees, and the Zeeman sextets from a- and d-sites begin to split into two sub-sextets, which is helpful to explain the phenomenon observed in the study of the magnetic property.