Effect of annealing treatment on transparent and conductive hydrated magnesium-carbon films

Transparent electronic technology has many urgent optoelectronic device applications. A key component of plasmonic materials in conventional semiconductors is the wide band gap of oxide thin films. Although transparent electronic materials have been developed for visible and near-infrared wavelengths, systems incorporating mid-infrared and far-infrared spectra are difficult to achieve. In this study, hydrated magnesium-carbon films, a new type of non-oxide transparent conductive thin films with a magnesium hydroxide structure, were generated using the three-step method. After annealing treatment, larger crystals in the thin films typically exhibited superior film resistivity, with conductivity values of approximately 8.63 × 10⁻³ Ω m. Due to the free electron concentration was not more than 10²⁰ cm⁻³, the films demonstrated excellent optical properties, with plasma wavelength values of approximately 8 μm for infrared transmittance above 70%. After annealing, due to the Moss-Burstein (M-B) effect, the visible light transmittance was greater than 85% and the optical bandgap shifted towards the blue region. In addition, the influences of the sputtering power of the carbon target on the properties of hydrated magnesium-carbon film were also discussed in this paper.