Chelating Dual Interface for Efficient and Stable Crystal Growth and Iodine Defect Management in Sn-Pb Perovskite Solar Cells

Suppressing Sn²⁺ oxidation and rationally controlling the crystallization process of tin-lead perovskite (Sn-Pb PVK) films by suitable bonding methods have emerged as key approaches to achieving efficient and stable Sn-Pb perovskite solar cells (PSCs). Herein, the chelating coordination is performed at the top and bottom interfaces of Sn-Pb PVK films. The chelation strength is stronger toward Sn²⁺ than Pb²⁺ by introducing oligomeric proanthocyanidins (OPC) at the bottom interface. This difference in chelation strength resulted in a spontaneous gradient distribution of Sn/Pb within the perovskite layer during crystallization, particularly enhancing the enrichment of Sn²⁺ at the bottom interface and facilitating the extraction and separation of photogenerated charge carriers in PSCs. Simultaneously, this top-down distribution of gradually increasing Sn content slowed down the crystallization rate of Sn-Pb PVK films, forming higher-quality films. On the top interface of the PVK, trifluoroacetamidine (TFA) was used to inhibit the generation of iodine vacancies (V_I) through chelating with surface-uncoordinated Pb²⁺/Sn²⁺, further passivating defects while suppressing the oxidation of Sn²⁺. Ultimately, the PSCs with simultaneous chelation at both top and bottom interfaces achieved a power conversion efficiency (PCE) of 23.31% and an open-circuit voltage (V_OC) exceeding 0.90 V. The stability of unencapsulated target devices in different environments also improved.