title = "Characterization of (α+β)/β transformation in a TC11 titanium alloy",
abstract = "(α+β)/β phase transformation temperature of a TC11 titanium alloy was confirmed to be 1035°C, which was obtained by three methods including the calculation method, differential scanning calorimetry and metallographic techniques. Based on this result, annealing treatments below and above the (α+β)/β phase transformation temperature were carried out, and the microstructure of the TC11 alloys before and after annealing treatment was analyzed by SEM. The result showed that conventional annealing below 1035°C does not change the Widmanstaten structure of TC11 alloy, though the thickness of a lamellar structure becomes thicker with increasing the annealing temperature. The microstructure of the TC11 alloy treated by annealing above the α+β/β transformation temperature is non-uniform because of the different forming temperature and growing duration of a phase in the TC11 alloy.",
keywords = "Annealing, Microstructure, Phase transformation, Titanium alloy",
author = "L. Geng and B. Xu and Li, \{Y. T.\} and Li, \{A. B.\} and Wang, \{G. S.\}",
year = "2007",
doi = "10.4028/3-908451-33-7.91",
language = "英语",
isbn = "9783908451334",
series = "Solid State Phenomena",
publisher = "Trans Tech Publications Ltd",
pages = "91--96",
booktitle = "Designing of Interfacial Structures in Advanced Materials and their Joints - Proceedings of the Int. Workshop on Designing of Interfacial Structures in Advanced Materials and their Joints, DIS'06",
address = "瑞士",
note = "International Workshop on Designing of Interfacial Structures in Advanced Materials and their Joints, DIS'06 ; Conference date: 18-05-2006 Through 20-05-2006",
}