Brazing of Al₂O₃ to Ti-6Al-4V alloy with in situ synthesized TiB-whisker-reinforced active brazing alloy

65.9Cu-24.4Ti-9.7TiB₂ (wt.%) composite filler was used to join Al₂O₃ and Ti-6Al-4V alloy. 30 vol.% TiB whiskers were in situ synthesized as reinforcements in joints. Brazing temperature was 890 °C, 910 °C, 930 °C, 950 °C and 970 °C, and the holding time was 0, 5, 10, 20, and 30 min. The microstructure and mechanical properties of brazed joints were analyzed by scanning electron microscope equipped with energy dispersive spectrometer, shear test and nano-indentation test. Results show that reaction layer Ti₄(Cu,Al)₂O forms at Al ₂O₃/brazing alloy interface. The reaction between TiB ₂ powders and Ti atoms in brazing alloy brings on in situ synthesizing TiB whiskers in (Ti,Al)₂Cu and AlCu₂Ti intermetallics. Formation of TiB whiskers minimizes the mismatch of thermal expansion coefficient between Al₂O₃ and brazing alloy, and makes the ductile-rigid-ductile multiple layer present in joints, which reduces residual stress of joints. The maximum shear strength of joints can reach 143.3 MPa when the brazing temperature is 930 °C, and holding time is 10 min.