An in situ bulk Zr₅₈Al₉Ni₉Cu₁₄Nb₁₀ quasicrystal-glass composite with superior room temperature mechanical properties

An in situ bulk Zr₅₈Al₉Ni₉Cu₁₄Nb₁₀ quasicrystal-glass composite has been fabricated by means of copper mould casting. The microstructure and constituent phases of the alloy composite have been analyzed by using X-ray diffraction, transmission electron microscopy and high-resolution transmission electron microscopy. Icosahedral quasicrystals were found to be the majority phase and the grain size is in half-μm scale. In between the I-phase grains is a glassy phase. Optical microscopy and scanning electron microscopy revealed that the as-cast alloys were pore-free. The microhardness of the composite is about 5.90 ± 0.30 GPa. The room temperature compression stress-true strain curve exhibits a 2% elastic deformation up to failure, and a maximum fracture stress of 1850 MPa at a quasi-static loading rate of 4.4 × 10^-4 s^-1. The mechanical property is superior to the early developed quasicrystal alloys, and is comparable to Zr-based bulk metallic glasses and their nanocomposites. The quasicrystal-glass composite exhibits basically a brittle fracture mode at room temperature.