氩气雾化Ti-48Al合金液滴的快速冷却和凝固组织

An analytical approach was developed to investigate nucleation and growth of Ti-48Al (atom fraction/%) alloy droplets during their flight in an argon atomization process. Evolution of microstructure of the solidified powders was investigated by scanning electron microscopy (SEM), transmission electron microscopy (TEM) and electron back-scatter diffraction (EBSD). Newton cooling model based on the initial number of nuclei, liquid/solid interface velocity, cooling rate and size of droplets was established. The results show that statistical nucleation events increase exponentially with the increase of powders size, and the growth of nuclei is transformed from a twinned spherical segment into a concentric liquid/solid interface geometry. Temperature of atomized droplets decreases rapidly with the cooling rate of 10⁵-10⁶K•s^-1. Then temperature increases sharply to near the liquidus temperature during recalescence. When the recalescence is completed, the droplet solidifies at a relatively slower rate. Afterwards the cooling rate of the fully solid phase decreases to about 10⁵K•s^-1.